Scaffold nanofibrosi a base di maltodestrina per l'ingegneria tissutale cutanea

The purpose of the following thesis work was the development of electrospun nanofibers based on maltodextrin, to which were associated amino acids/poly amino acids (lysine, arginine and polylysine). Conductivity, surface tension and viscosity analyses were performed on polymeric solutions. The nanofibers were prepared by electrospinning, which allows the preparation of fibers from a polymer solution by the application of an electric field. The membranes have been morphologically characterized by scanning electron microscopy (SEM), evaluations of the mechanical strength of the membranes, and dimensional analysis of the fiber diameters have been performed.

Lo scopo del seguente lavoro di tesi è stato lo sviluppo di nanofibre elettrofilate a base di maltodestrina, a cui sono stati associati aminoacidi/poli aminoacidi (lisina, arginina e polilisina). Sono state effettuate analisi di conducibilità, tensione superficiale e viscosità sulle soluzioni polimeriche. Le nanofibre sono state preparate mediante elettrofilatura, che consente la preparazione di fibre a partire da una soluzione polimerica mediante l'applicazione di un campo elettrico. Le membrane sono state caratterizzate morfologicamente mediante microscopia elettronica a scansione (SEM), sono state effettuate valutazioni della resistenza meccanica delle membrane, e dell'analisi dimensionale dei diametri delle fibre.