Sintesi e proprietà della perovskite nanocristallina Cs4SnBr6

During my training I worked on the synthesis and the characterization of lead-free perovskite nanocrystals based on bivalent tin for applications in technological fields (solar cells, LEDs, transistors). In particular, I studied Cs4SnBr6 that in literature is present only in the bulk form. At the moment, the perovskites presenting best performances in technological applications, due to their optical properties, are based on lead and they reach a quantum efficiency about 90-95%. The aim of the scientific research is replacing lead with non-toxic cations such as tin, but reaching comparable performances, a result not yet obtained.

Il lavoro svolto durante l'internato di tesi è incentrato sulla sintesi e la caratterizzazione di nanocristalli di perovskite non contenenti piombo, basati sullo stagno bivalente, per applicazioni in campo tecnologico (celle solari, LED, transistor). Nello specifico il mio studio ha riguardato la perovskite Cs4SnBr6, che in letteratura è presente solo nella forma bulk. Le perovskiti che al momento presentano le migliori prestazioni in applicazioni tecnologiche, dovute alle proprietà ottiche, sono basate sul piombo e raggiungono efficienze quantiche del 90-95%. Lo scopo della ricerca scientifica è quello di riuscire a sostituire il piombo con cationi non tossici come lo stagno, arrivando però a prestazioni paragonabili, un risultato che non è ancora stato ottenuto.