The thesis work consists in the characterization of superelastic Nitinol threads, both commercial and new generation, before and after some surface finishing treatments. The analysis was focused both on the study of mechanical and functional properties and on the evolution of fatigue behavior. Particular attention was paid to the texture generated during the semi-finished processes that led to the realization of the threads in question. Equally important was the fractographic analysis of the size and nature of the defects that caused cracks in the stranded strands. These dimensions have finally been related to fatigue life, obtaining a trend in good agreement with the historical data.
Il lavoro di tesi consiste nella caratterizzazione di fili di Nitinol superelastico, sia commerciali che di nuova generazione, prima e dopo alcuni trattamenti di finitura superficiale. L’analisi è stata focalizzata sia sullo studio delle proprietà meccaniche e funzionali che sull’evoluzione del comportamento a fatica. Particolare attenzione è stata posta alla texture generatasi durante i processi dei semilavorati che hanno portato alla realizzazione dei fili in esame. Altrettanto importante è stata l'analisi frattografica della dimensione e natura dei difetti che hanno causato rotture nei fili testati a fatica. Tali dimensioni sono infine state correlate alla vita a fatica ottenendo un andamento in ottimo accordo con i dati storici
Studio e caratterizzazione degli effetti di inclusioni e finitura superficiale su microstruttura e proprietà funzionali di fili in Nitinol superelastico per applicazioni biomediche
CRESCI, MATTEO
2017/2018
Abstract
The thesis work consists in the characterization of superelastic Nitinol threads, both commercial and new generation, before and after some surface finishing treatments. The analysis was focused both on the study of mechanical and functional properties and on the evolution of fatigue behavior. Particular attention was paid to the texture generated during the semi-finished processes that led to the realization of the threads in question. Equally important was the fractographic analysis of the size and nature of the defects that caused cracks in the stranded strands. These dimensions have finally been related to fatigue life, obtaining a trend in good agreement with the historical data.È consentito all'utente scaricare e condividere i documenti disponibili a testo pieno in UNITESI UNIPV nel rispetto della licenza Creative Commons del tipo CC BY NC ND.
Per maggiori informazioni e per verifiche sull'eventuale disponibilità del file scrivere a: unitesi@unipv.it.
https://hdl.handle.net/20.500.14239/24194